Good resistance against corrosion and oxidation, e.g. in vanadium or sulphur vapor up to 980°C. Good bonding. Coating of boiler tubes, finned tubes, super heat tubes.

Coating of heating elements and strip conductors on ceramics, can be sprayed relatively cold, therefore heat adding can be reduced during the spraying process. Resistant against Gas corrosion, oxidation stability up to 870 °C also under atmospheres with Vanadium and sulphur impurity. High conducting capacity, rapid machining, good adhesive characteristics.

Salvage and build-up of worn or mismatched parts, Coating of shafts, ball bearing caps, valve spindles and pistons. Microporose layer structure, high wear resistance in lubricated wear systems, rapid machining, max. layer thickness 2 mm.

Iron based Flux-cored wire with a high content of chrome for high wear and corrosion resistance. Can be applied by Arc-, Wire flame- or High-Velocity-Wire flame-Spraying (HVWFS). Layers with porosity lower than 10% are available with hardness of up to 52HRC. Wear and corrosion resistant coatings of feeding systems, e.g. for the chemical industry.

Austenitic stainless steel similar to type 316. Resistance against corrosion. Good machining properties. Salvage and build-up of worn or mismatched parts.

Stainless steel with high resistance against corrosion has low shrinkage and good mach inability. Salvage and build-up of worn or mismatched parts.

Iron based Flux-cored wire with a high content of carbon and chrome for high wear and corrosion resistance. Can be applied by Arc-, Wire flame- or High-Velocity-Wire flame- Spraying (HVWFS). Coatings with porosity lower than 10% are available with hardness of up to 55HRC.

Thermal coating with high resistance against mineral wear and friction. Excellent wearing qualities and fair corrosion resistance. Salvage and build-up of worn or mismatched parts.

Coating of Heating elements and strip conductors on ceramics, can be sprayed relatively cold, therefore heat adding can be reduced during the spraying process. Resistant against Gas corrosion, oxidation stability up to 870 °C also under atmospheres with Vanadium and sulphur impurity. High conducting capacity, rapid machining, good adhesive characteristics.

Fluxed-cored wire with 50% FTC for high resistance against abrasion. Can be applied by Arc-, Wire flame- or High-Velocity-Wire flame-Spraying (HVWFS). Coatings with porosity lower than 10% are available with hardness of up to 60HRC.

DURMAT AS-890 provides good abrasion and corrosion resistant coatings. Surface can be polished. Ductile and heat resistant up to 870°C. Increasing hardness after extended use. The surface shows chrome like finishing after grinding. Universal Application where extreme hard, corrosion resistant combined with good heat resistant is required. Good bond strength and impressive elasticity for a coating like that.

Abrasion and corrosion resistant coatings polish able surfaces, ductile, heat resistant up to 870 °C. Universal Application where extreme hard, corrosion resistant and heat resistant coatings are required.

Extreme high resistance against abrasion, high adhesive characteristics, Anti-Sliding characteristics, high Spray rate. Anti-Sliding surfaces on platforms in industrial premises and on footpaths on ship decks.

DURMAT AS-898 produces a hard, abrasive and corrosion resistant coating. In service the hardness is increasing. Conventional machining and polishing techniques provide high chrome like finishes. Typical applications use coating thicknesses up to 0.100 mm on boiler tubes, food, paper, drums and rolls, shafts in a marine environment are also sprayed with this material.